Sampling or task jitter affects the performance of digital control systems but realistic simulation of this effect has not been possible to date. Our previous work has developed a novel method to simulate sampling jitter in MATLAB/Simulink simulation software where the jitter is generated randomly. What has been missing is a way to capture sampling jitter from a target platform and then feed this timing information into the simulation. This paper presents a low-cost and novel solution to these problems. The method uses an Arduino board to capture task jitter from two different hardware platforms with multiple stressing conditions. Then the recorded performance data is used to drive realistic simulations of a control system. Measurement shows that the task jitter data does not follow any specific random distribution such as Gaussian or Uniform. Furthermore, very occasional timing patterns, which may not be picked up while testing a real system, can result in extreme controller responses. This novel method allows comparisons of different platforms and reduces the effort required to choose the most appropriate platform for full implementation.

     

Inconel 690传热管GTAW对接焊接头组织及力学性能研究

对Inconel 690传热管材进行钨极气体保护焊(GTAW)对接焊,采用拉伸试验机、压扁试验机和光学显微镜测试和分析传热管焊接接头,同时利用ANSYS软件开展焊接接头在设计工况失压时的一次应力强度校核。研究结果表明:焊缝中心为树枝胞状晶,熔合线附近为粗大柱状晶。室温时接头的平均抗拉强度为619 MPa,平均屈服强度为292 MPa,350℃时接头平均抗拉强度为475 MPa,平均屈服强度为206 MPa,拉伸接头断裂从熔合区开始贯穿整个焊缝组织,呈塑性断裂。压扁试验和反向压扁试验结果表明管接头完好。通过ANSYS分析可知,设计工况下传热管接头350℃许用应力强度150 MPa限值可满足其一次应力强度要求,且裕量较大。     

Pseudocapacitive contributions to electrochemical kinetics in NiOx electrochromic anodes

Because of its ability to change optical absorption dynamically by applied electric field, nickel oxide (NiO) is a promising anodic material in smart windows, which can improve energy conversion efficiency in construction buildings. Although many works have achieved high electrochromic performance with different method. The underlying mechanism is still not fully investigated. In this article, we prepared the NiO films with large specific surface area and high stability by electron beam evaporation. X-ray diffraction (XRD), scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS) were employed to figure out the surface morphology and composition of as-deposited films. Afterwards, the electrochemical properties and optical performance of the prepared NiO films were investigated. On this basis, the origin of surface charge was fully analyzed by cyclic voltammetry and diffusion coefficient test. These experimental and theoretical results firmly confirm that both the surface reaction and capacitive effect bring about the excellent EC performance in NiO films. These results not only provide clear evidence about electrochemical kinetics in NiO films, but also offer some useful guidelines for the design of EC materials with higher performance and longer stability.     

Synergistic effect of bulk phase doping and layered-spinel structure formation on improving electrochemical performance of Li-Rich cathode material

In this study, La was doped into the lithium layer of Li-rich cathode material and formed a layered-spinel hetero-structure. The morphology, crystal structure, element valence and kinetics of lithium ion migration were studied by field emission scanning electron microscope (FESEM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS) and electrochemical impedance spectroscopy (EIS). The La doped lithium-rich cathode material exhibited similar initial discharge capacity of 262.8 mAh g^?1 at 0.1 C compared with the undoped material, but the discharge capacity retention rate can be obviously improved to 90% after 50 cycles at 1.0 C. Besides that, much better rate capability and Li⁺ diffusion coefficient were observed. The results revealed that La doping not only stabilized the material structure and reduced the Li/Ni mixing degree, but also induced the generation of spinel phase to provide three-dimensional diffusion channels for lithium ion migration. Moreover, the porous structure of the doped samples also contributed to the remarkable excellent electrochemical performance. All of these factors combined to significantly improve the electrochemical performance of the material.     

Colossal dielectric response and relaxation behavior in novel system of Zr4+ and Nb5+ co-substituted CaCu3Ti4O12 ceramics

In this work, we developed a novel system of isovalent Zr⁴⁺ and donor Nb⁵⁺ co-doped CaCu₃Ti₄O₁₂ (CCTO) ceramics to enhance dielectric response. The influences of Zr⁴⁺ and Nb⁵⁺ co-substituting on the colossal dielectric response and relaxation behavior of the CCTO ceramics fabricated by a conventional solid-phase synthesis method were investigated methodically. Co-doping of Zr⁴⁺ and Nb⁵⁺ ions leads to a significant reduction in grain size for the CCTO ceramics sintered at 1060 °C for 10 h. XRD and Raman results of the CaCu₃Ti_3.8-xZr_xNb_0.2O₁₂ (CCTZNO) ceramics show a cubic perovskite structure with space group Im-3. The first principle calculation result exhibits a better thermodynamic stability of the CCTO structure co-doped with Zr⁴⁺ and Nb⁵⁺ ions than that of single-doped with Zr⁴⁺ or Nb⁵⁺ ion. Interestingly, the CCTZNO ceramics exhibit greatly improved dielectric constant (~10⁵) at a frequency range of 10²–10⁵ Hz and at a temperature range of 20–210 °C, indicating a giant dielectric response within broader frequency and temperature ranges. The dielectric properties of CCTZNO ceramics were analyzed from the viewpoints of defect-dipole effect and internal barrier layer capacitance (IBLC) model. Accordingly, the immensely enhanced dielectric response is primarily ascribed to the complex defect dipoles associated with oxygen vacancies by co-doping Zr⁴⁺ and Nb⁵⁺ ions into CCTO structure. In addition, the obvious dielectric relaxation behavior has been found in CCTZNO ceramics, and the relaxation process in middle frequency regions is attributed to the grain boundary response confirmed by complex impedance spectroscopy and electric modulus.     

特低渗砂岩油藏CO2-低界面张力黏弹流体协同驱油机理研究

目的特低渗油藏储层物性差、层间非均质性强,造成CO₂驱易发生气窜,提高采收率效果欠佳,其中,CO₂水气交替驱作为结合CO₂驱和水驱优势的方法,具有较高的适用性。为进一步改善CO₂-水交替驱的开发效果,开展了CO₂-低界面张力黏弹流体协同驱油研究。 方法通过界面张力和润湿性能测试评价低界面张力黏弹流体基本性能,并利用微观可视化驱油实验及岩心驱油实验等,探究了不同驱替方式的驱油效果和CO₂-低界面张力黏弹流体协同驱油过程中二者之间的“协同作用”机理。 结果低界面张力黏弹流体具备良好的界面活性和改变岩石表面润湿性能力,水驱后开展CO₂驱、低界面张力黏弹流体驱、CO₂-低界面张力黏弹流体交替协同驱,采收率可在水驱基础上分别提高0.91%、10.66%、16.25%,其提高采收率机理包括降低界面张力、改善流度比、改变岩石表面润湿性及乳化作用的协同效应等。 结论CO₂-低界面张力黏弹流体协同驱既可有效增强非均质特低渗砂岩油藏注CO₂过程中气体流动性控制,又能够降低CO₂萃取轻烃导致重质组分沉积的影响,具有协同增效作用。      

High-Performance Solution-Processed Nondoped Circularly Polarized OLEDs with Chiral Triptycene Scaffold-Based TADF Emitters Realizing Over 20% External Quantum Efficiency

Recently, circularly polarized organic light-emitting diodes (CP-OLEDs) fabricated with thermally activated delayed fluorescence (TADF) emitters are developed rapidly. However, most devices are fabricated by vacuum deposition technology, and developing efficient solution-processed CP-OLEDs, especially nondoped devices, is still a challenge. Herein, a pair of triptycene-based enantiomers, (S,S)-/(R,R)-TpAc-TRZ, are synthesized. The novel chiral triptycene scaffold of enantiomers avoids their intermolecular π–π stacking, which is conducive to their aggregation-induced emission characteristics and high photoluminescence quantum yield of 85% in the solid state. Moreover, the triptycene-based enantiomers exhibit efficient TADF activities with a small singlet-triplet energy gap (ΔE_ST) of 0.03 eV and delayed fluorescence lifetime of 1.1 µs, as well as intense circularly polarized luminescence with dissymmetry factors (|g_PL|) of about 1.9 × 10⁻³. The solution-processed nondoped CP-OLEDs based on (S,S)-/(R,R)-TpAc-TRZ not only display obvious circularly polarized electroluminescence signals with g_EL values of +1.5 × 10⁻³ and −2.0 × 10⁻³, respectively, but also achieve high efficiencies with external quantum, current, and power efficiency up to 25.5%, 88.6 cd A⁻¹, and 95.9 lm W⁻¹, respectively.     

Nanovaccine-Mediated Cell Selective Delivery of Neoantigens Potentiating Adoptive Dendritic Cell Transfer for Personalized Immunization

Neoantigen vaccines and adoptive dendritic cell (DC) transfer are major clinical approaches to initiate personalized immunity in cancer patients. However, the immunization efficacy is largely limited by the in vivo trajectory including neoantigens’ access to resident DCs and DCs’ access to lymph nodes (LNs). Herein, an innovative strategy is proposed to improve personalized immunization through neoantigen-loaded nanovaccines synergized with adoptive DC transfer. It is found that it enables selective delivery of neoantigens to resident DCs and macrophages by coating cancer cell membranes onto neoantigen-loaded nanoparticles. In addition, the nanovaccines promote the secretion of chemokine C-C motif ligand 2 (CCL2), CCL3, and C-X-C motif ligand 10 from macrophages, thus potentiating the access of transferred DCs to LNs. This immunization strategy enables coordinated delivery of identified neoantigens and autologous tumor lysate-derived undefined antigens, leading to initiation of antitumor T cell immunity in a personalized manner. It significantly inhibits tumor growth in prophylactic and established mouse tumor models. The findings provide a new vision for potentiating adoptive cell transfer by nanovaccines, which may open the door to a transformative possibility for improving personalized immunization.     

Phase and microstructure evolution of Sc2O3–CeO2 –ZrO2ceramics in Na2SO4 + V2O5 molten salts

In this study, the destabilization resistance of Sc₂O₃ and CeO₂ co-stabilized ZrO₂ (SCZ) ceramics was tested in Na₂SO₄ + V₂O₅ molten salts at 750°C–1100 °C. The phase structure and microstructure evolution of the samples during the hot corrosion testing were analyzed with X-ray diffraction (XRD), Raman spectra, scanning electron microscopy (SEM), energy dispersive X-ray spectrum (EDS), and X-ray photoelectron spectroscopy (XPS). Results showed that the destabilization of SCZ ceramics at 750 °C was the result of the chemical reaction with V₂O₅ to produce m-ZrO₂ and CeVO₄, and little ScVO₄ was detected in the Sc₂O₃-rich SCZ ceramics. The primary corrosion products at 900 °C and 1100 °C were CeO₂ and m-ZrO₂ due to the mineralization effect. The Sc₂O₃-rich SCZ ceramics exhibited excellent degradation resistance and phase stability owing to the enhanced bond strength and the decreased size misfit between Zr⁴⁺ and Sc³⁺. The destabilization mechanism of SCZ ceramic under hot corrosion was also discussed.     

Enhanced thermal shrinkage behavior of phenolic-derived carbon aerogel-reinforced by HNTs with superior compressive strength performance

A novel carbon/m-HNTs composite aerogel was synthesized by introducing the modified halloysite nanotubes (m-HNTs) into phenolic (PR) aerogels through chemical grafting, followed with carbonization treatment. In order to explore the best proportion of HNTs to phenolic, the micromorphology of PR/m-HNTs were investigated by SEM before carbonization, confirming 10 wt% of m-HNTs is most beneficial to the porous network of aerogels. The interaction between PR and HNTs was studied by FTIR spectra, and microstructure evolution of the target product-carbon/m-HNTs composite aerogel were illustrated by SEM and TEM techniques. SEM patterns indicated that the carbon/m-HNTs aerogels maintain a stable porous structure at 1000 °C (carbonization temperature), while a ~20 nm carbon layer was formed around m-HNTs generating an integral unit through TEM analysis. Specific surface area and pore size distribution of composite aerogels were analyzed based on mercury intrusion porosimetry and N₂ adsorption–desorption method, the obtained results stayed around 500 m²g^?1 and 1.00 cm³g^?1 (pore volume) without significant discrepancy, compared with pure aerogel, showing the uniformity of pore size. The weight loss rate (26.76%) decreased greatly compared with pure aerogel, at the same time, the best volumetric shrinkage rate was only 30.83%, contributed by the existence of HNTs supporting the neighbor structure to avoid over-shrinking. The highest compressive strength reached to 4.43 MPa, while the data of pure aerogel was only 1.52 MPa, demonstrating the excellent mechanical property of carbon/m-HNTs aerogels.